Preclinical evaluation of a 3D-printed hydroxyapatite/poly(lactic-co-glycolic acid) scaffold for ridge augmentation

Po Chun Chang, Hui Ting Luo, Zhi Jie Lin, Wei Chiu Tai, Ching He Chang, Ying Chieh Chang, David L. Cochran, Min Huey Chen

Producción científica: Articlerevisión exhaustiva

12 Citas (Scopus)

Resumen

Background/Purpose: Supracrestal ridge augmentation (SRA) is a major challenge for clinicians. This study investigated the efficacy of a 3D-printed (3DP) hydroxyapatite/poly(lactic-co-glycolic acid) (HA/PLGA) scaffold as a potential biologic for SRA. Methods: Scaffolds that were 5 mm in diameter and 2.5-mm thick with a 1.2-mm diameter through-and-through central hole composed of 90% HA and 10% PLGA were printed using an extrusion-based bioprinter. The HA/PLGA scaffold was fixed with a 1.2-mm titanium mini-implant on the buccal surface of rat mandible (Ti-HPS), and the outcome of SRA were compared with sites treated with a titanium mini-implant alone (control) and a titanium mini-implant covered with deproteinized bovine bone-derived matrix (Ti-DBBM) at 4 and 8 weeks by microcomputed tomography (micro-CT), back-scattered SEM, and histology assessments. Results: The HA/PLGA scaffolds were 2.486 ± 0.082 mm thick with an outer diameter of 4.543 ± 0.057 mm and an inner diameter of 1.089 ± 0.045 mm, and the pore dimensions were 0.48–0.52 mm. There was significantly more mineralized tissue in the Ti-DBBM and Ti-HPS groups than in the control group at both time points. Newly formed bone (NB) was well-integrated with the DBBM and HA/PLGA scaffolds. The framework of the 3DP-HA/PLGA scaffold remained in place, and NB-implant contact (NBIC) was advanced to the middle level in the Ti-HPS group until 8 weeks, whereas dispersion of DBBM with a lower level NBIC was noted in the Ti-DBBM group at both time points. Conclusion: The 3DP HA/PLGA scaffold maintains supracrestal space and demonstrates osteoconductivity to facilitate SRA.

Idioma originalEnglish (US)
Páginas (desde-hasta)1100-1107
Número de páginas8
PublicaciónJournal of the Formosan Medical Association
Volumen120
N.º4
DOI
EstadoPublished - abr 2021

ASJC Scopus subject areas

  • General Medicine

Huella

Profundice en los temas de investigación de 'Preclinical evaluation of a 3D-printed hydroxyapatite/poly(lactic-co-glycolic acid) scaffold for ridge augmentation'. En conjunto forman una huella única.

Citar esto